A brief introduction
Ceramic foam filter is a special technology. It has a foam-like porous structure of ceramic products, and its light weight, chemical stability, large surface area through-hole rate, corrosion resistance, high strength, good thermal shock resistance characteristics. Divided into two shapes: round specifications, square specifications and weaving way: honeycomb.
Ceramic foam filter with a high temperature, corrosion resistance, resistance to molten metal erosion, high strength, high pass rate, and the characteristics of the large surface area is mainly used in the field of metallurgy and casting metal liquid filtration and purification. The flow of a mixture of molten metal passes through foam ceramic porous structure becomes uniform smooth clean molten metal filled the mold to remove the molten steel in the fineness of micron inclusions and some parcels gas reduce the erosion of the sand mold, and reduce product obsolescence rate. Ceramic foam filters can be made of different pore size and porosity, in order to obtain satisfactory filtration effect.
Ceramic foam material
Ceramic foam filter, depending on the materials: alumina foam ceramic filters, silicon carbide ceramic foam filter, zirconia ceramic foam filter, and magnesium oxide foam ceramic filter.
- In the bronze casting process, the use of silicon carbide ceramic foam filter material is of SiC.
- Steel castings uses zirconia ceramic foam filters. Zirconia ceramic foam filters material of ZrO2 zirconia. Zirconia heat-resistant temperature of the filter is higher than about 1760 ° C, with very high strength and excellent high-temperature impact.
- Alumina ceramic foam filter products effectively remove solid-state mixed with the molten metal, so aluminum alloy can be successfully forged, aluminum foil manufacturing, extrusion processing technology, perfect aluminum products. 10ppi coarse porosity 70ppi of fine porosity range of options
|Foam ceramic material||Alumina||Silicon Carbide||Zirconium Oxide|
|Application||Alumina or aluminium alloy casting||Iron or iron alloy casting||Steel ,stainless steel and synthetic steel casting|
|Holes density (ppi)||10 to 50||10 to 45||10 to 30|
|Working temperature (0C)||1200||1500||1750|
|Thermal shock resistance (times/11000C)||>6||>6||>7|
|Compressive strength (Mpa)||0.8||0.9||0.8 to 1.0|
|Bending strength (Mpa)||0.6||0.8||1.0 to 1.2|
|Regular product size(mm)||Round Shape: Ф40×12, Ф45×15, Ф50×15, Ф55×15, Ф60×15, Ф70×20, Ф90×20, Ф150×25, Ф200×25|
|Square shape: L×W×T L=40-500 mm W=40-500 mm T=10-50 mm|